• 基于熔融接枝烷基链提升聚丁烯发泡行为研究,韩冲 孙并臻 宫瑞英 李朝旭,高分子学报,2020
    聚烯烃材料引入长支化结构,能够提升材料熔体强度和异相成核作用,使聚合物具备更加优异的发泡性能,从而扩宽材料的应用领域. 本文利用甲基丙烯酸十八烷基酯(SMA)熔融改性聚丁烯(PB),发现其链段缠结程度提升,发泡行为改善. 通过红外谱图的化学结构分析以及材料的力学性能分析,发现随着SMA添加量的增加,材料拉伸强度降低,冲击强度呈现先升高后降低的趋势. 差示扫描量热(DSC)的分析结果表明改性PB的结晶度下降. 采用间歇釜式法制备PB发泡珠粒,利用扫描电子显微镜(SEM)研究发泡珠粒泡孔结构,结果表明:SMA改性后,发泡珠粒平均泡孔尺寸、孔径分布、泡孔密度都得到改善,发泡温度窗口加宽且发泡稳定性提升. 当添加SMA达到3份时,珠粒......
    lchaoxu 写于2020.06.18
    1035 1035 0
  • Amino acid modified graphene oxide for assembly of nanoparticles for wastewater treatment.Applied Surface Science,2020,Lili Lv, Xiaochen Wu, Xiangsheng Han, Chaoxu Li,DOI:10.1016/j.apsusc.2020.147620
    The surface modifications of graphene oxide (GO) by biomolecules are widely used to increase the biocompatibility, change the hydrophobicity, solubility and surface properties of GO, and provide GO with selectivity to specific molecules. A simple, biocompatible and reproducible way to decorate GO was introduced with......